Mae'r gofynion ar gyfer deunyddiau crai fel a ganlyn:
(1) Mae rhostio molybdenwm yn gofyn am S<0.10%, Cu<0.6%, and Pb<0.5%. The actual ingredients are: Mo48.5%~52%, S0.04%~0.07%, P0.01%~0.02%, Cu0.1%~0.5%, Pb0.2%~0.5%, FeO3%~5%, SiO28%~14%, CaO2%~4.5%. 5% to 10% of the total molybdenum is in the form of MoO2, which should be considered when calculating the reaction heat. The particle size is <15mm, of which >10mm yn cyfrif am lai na 10%, a<2mm accounts for about 60%. (2) Ferrosilicon powder contains Si75%~77%; the particle size is <1mm.
pris ferro molybdenwm powdr
(3) Aluminum particles contain Al>90% a Cu<0.1%; the particle size is <3mm, and the part <0.5mm shall not exceed 30%.
(4) Iron ore contains Fe>65%, S<0.05%, P<0.05%, C<0.30%; particle size<1mm. Iron oxide scale or iron concentrate can be used instead.
(5) Mae'r sgrapiau dur yn sgrapiau dur carbon cyffredin, ac mae hyd y cyrl<50mm.
(6) Fluorite contains CaF2>90%. Maint gronynnau<3mm.
Pris aloi Ferro Molybdenwm
(7) Saltpeter contains NaNO3>90%. Rhaid sychu'r holl ddeunyddiau crai yn drylwyr a rhaid iddynt beidio â chynnwys lleithder er mwyn osgoi tasgu a damweiniau yn ystod y broses fwyndoddi. Mae'r deunyddiau crai yn cael eu pwyso'n gywir yn ôl y gyfran a gyfrifwyd, eu rhoi yn y cymysgydd a'u cymysgu'n gyfartal, yna eu rhoi yn y ffwrnais mwyndoddi, a'u mwyndoddi gan ddefnyddio'r dull tanio uchaf.